MALZEMENİN |
MALZEMENİN |
|||||||||
DIN |
AISI/SAE |
EN |
C |
Si |
Mn |
Pmax |
Smax |
Cr |
Mo |
Nmax |
1.0908 |
9262 |
60SiMn5 |
0.55 - |
1.00 - |
0.90 - |
0.050 |
0.050 |
- |
- |
0.007 |
1.7176 |
9260 |
55Cr3 |
0.52 - |
0.15 - |
0.70 - |
0.035 |
0.035 |
0.60-0.90 |
- |
- |
1.8159 |
6150 |
50CrV4 |
0.47 - |
≤ 40 |
0.70 - |
0.035 |
0.035 |
0.90-1.20 |
- |
- |
1.1231 |
1070 |
CK67 |
0.65 - |
0.15 - |
0.60 - |
0.035 |
0.035 |
- |
- |
- |
1.0902 |
- |
46Si7 |
0.42 - |
1.50 - |
0.50 - |
0.050 |
0.050 |
- |
- |
0.007 |
1.7701 |
- |
51CrMoV7 |
0.48 – 0.56 |
0.15 - |
0.70 - |
0.035 |
0.035 |
0.90-1.20 |
0.15-0.25 |
- |
1.8161 |
- |
58CrV4 |
0.55 - |
0.15 - |
0.70 - |
0.035 |
0.035 |
0.90-1.20 |
- |
- |
1.0961 |
- |
60SiCr7 |
0.55 - |
1.50 - |
0.70 - |
0.045 |
0.045 |
0.20-0.40 |
- |
0.007 |
1.5028 |
- |
65Si7 |
0.60 - |
1.50 - |
0.70 - |
0.035 |
0.035 |
- |
- |
- |
1.7103 |
- |
67SiCr5 |
0.62 - |
1.20 - |
0.40 - |
0.035 |
0.035 |
0.40-0.60 |
- |
- |